New Surface Tolerant Technology Solves Maintenance Dilemma

belozona sept 2015 1Leaking oil tanks repaired in-situ with fast-curing epoxy composite

A UK oil supplier was faced with a major dilemma when a transformer oil storage tank began to leak in several places. As the tank was located in a confined space, it would be highly dangerous to repair the damage in-situ using hot work. If the tank was removed and repaired offsite, not only would this incur large amounts of downtime, but the cost of welding alone would be over £15,000.

The supplier required a bespoke in-situ repair solution that would safely repair and protect the steel tanks against corrosive attack for the long-term, whilst incurring minimum downtime. In addition to this, as the application area was highly contaminated with oil, the repair method needed to be compatible with this environment and provide a robust repair solution despite the contaminated surface.

Background Information

The supplier recycles millions of liters of transformer oil every year. This process works by extracting the moisture from recycled oil by shutting the tanks off from the atmosphere. The tanks are then connected to silica gel tanks to remove the moisture. As a result of this repeated process, several areas located at the seams of the steel tanks were beginning to corrode.

belozona sept 2015 2

Application Specification

Belzona 1212 was chosen to bond steel plates to the damaged areas followed by a protective coating using Belzona 5831 (ST-Barrier). Launched earlier this year, Belzona 1212 represents a milestone for epoxy technology as not only does this material provide excellent, long-term corrosion resistance, but it achieves this even when applied to oil contaminated surfaces where grit blasting is not possible. Coupled with the rapid cure feature ensuring minimal downtime, Belzona 1212 is the ideal solution to repair the leaking tank. Belzona 5831 was chosen to coat the repaired area as this surface tolerant epoxy coating is specially designed for the protection of oil contaminated surfaces.

Fast and Simple Application Method

The application was carried out by Belzona Technosol, Belzona’s application services division. Once the leaks were stemmed, the area was then cleaned and roughened to prepare the surface for the Belzona systems. Belzona 1212 was used to bond pre-manufactured steel plates onto the damaged areas. This was done by firstly applying a thin film of the epoxy system onto the prepared substrate, pushing the material well into the profile. Further material was then applied to the steel patch forming a peak of material at the centre. The patch was then pushed into place allowing the excess material to exude from beneath ensuring minimal air entrapment. The excess material was then removed and the system was allowed to cure before coating the area with Belzona 5831, providing long-term corrosion protection.

In-situ Repair Completed in Two Days

Osian Jones, Belzona Field Sales Engineer said: “If the oil supplier had chosen to use welding as the repair method, this could have taken weeks to complete, leading to big problems in terms of trying to stop moisture entering the tanks. The Belzona application was completed in just over two days without the tanks being taken offline. This ensured moisture ingress would not occur and allowed the plant to continue as normal with minimal disruption. Furthermore, the supplier was able to avoid a significant amount of capital expenditure as the Belzona repair method could be carried out at a fraction of the cost of welding.”